Fissure Sealant Interface Microleakage Using One step Adhesives

Sandy Christiono,drg,.SpKGA

Faculty of Dentistry, Islamic University of Sultan Agung

Semarang – Indonesia

Email: Sandy_dentistry@yahoo.com

 

Abstraks

This study evaluated the efficacy of a one step adhesives in reducing microleakage after  water storage and thermocycling. eighteen freshly extracted caries-free human premolars  were used. The teeth were randomly divided into two groups; Group I: control etch adhesive (GC),Group II: G Bond One step adhesive (GC) The teeth were restored using helioseal Vivadent. Group II Each layer was cured using the Spectrum 800 curing light (Dentsply/Caulk) for 20 seconds at 600mW/cm2. The teeth were stored in artifisial saliva for 7 days in incubator. Samples were thermocycled 250x between 5°C and 55°C with a dwell of 30 seconds, then placed in a 0.5% methylene blue dye solution for 24 hours at 37°C. Samples were sectioned longitudinally  and evaluated for microleakage at the occlusal and gingival margins under a microscope at 40x magnification. Dye penetration was scored: 0: no microleakage visible, score 1: microleakage up to half of the fissure, score 2: microleakage more than half of the fissure. Mann-Whitney test was used to demonstrate significantly more dye penetration in Group I and Group II. When comparing the scores for two group, the Mann Whitney test showed no significant difference in dye penetration for etch and One step adhesive (p>0.05). Based on the results of this study, it can be concluded that etc and one step adhesive in the fissure sealant no significant difference to reduce of microleakage in study in vitro.

 

Kata Kunci : Microleakage, fissure sealant, Resin Bis-GMA, one step adeshive, dye penetration

 

DAFTAR PUSTAKA

  1. Herle GP, Joseph T, Varma B, Jayanthi M. Comparetive Evaluation of Glass Ionomer and Resin Bis-GMA Fissuresealant Using Noninvasive and Invasive Techniques- A SEM and Mikroleakage Study. J Indian Soc Pedo Prey Dent 2004, 22 (2); p. 56-62
  2. Kaste LM. Coronal caries in primary and permanent dentition of children and adolescent 1-17 years of age. 1996: 631-634
  3. Kadiyanti,L. Gambaran Kebersihan Gigi dan Mulut, Frekuensi menyikat Gigi dan Karies pada Penderita Anak yang Datang ke Klinik Pedodonsia FKG Unair 1998, p. 23-24
  4. Deliperi S, DN Bardwell, C Wegley. Restoration Interface Mikroleakage Using Two Total Etch and Two Self Etch Adhesive.Operative Dentistry ,2007:174-      179
  5. Hatrick C.D. Dental Material; Clinical Application for Dental Assistants and Dental Hygienist, Saunders, 2003: 60-88
  6. Pazinatto F.B, Campos B.B. Effect of the number of Thermocycles on Microleakage of Resin composite restorations, pasqui. Odontol.bras, 2003, 17(4)
  7. Smith LA, OBrient, Retief. Mikroleakage of two dentinal bonding restorative system. J Dent. 2008,67;309
  8. Hermina M. Perbaikan sealant Resin Bis-GMA . Fakultas Kedokteran Gigi Bagian Pedodonsia USU. 2003: 1-2
  9. Vanessa P, Singorethi, pereira.. In Vitro Evaluation of Microleakage of Different Materials Used as Pit-and-Fissure Sealant. Braz Dent J 2006,17(1): 49-52
  10. Hevinga M.A., .2007 : Microleakge and sealant penetration in contaminated carious fissures. Journal of dentistry. 2007, 909 – 914
  11. Nahid A, Negar, NorouZi,. The Effect of Bonding Agent on the microleakage of sealant following contamination with saliva, J Indian Soc Pedod prevent          dent. 2008
  12. Laurence, Michele, Marrie, Thomas. Journal of adhesive dentistry .2004, 6 (1) : 43-48 ;
  13. Mc Donal, R. And Avery, D. R.. Dentistry for the child and Aldolescent. 8 th ed St Louis, Mosby Years Book, Inc, 2004: 357-360
  14. Droz, Bouter D, Courson F.. In Vitro Mikroleakage of two sealant : first result of a multicentrik study. Journal European cells and material vol 10. 2005:.15
Leave a reply